Interface-Mediation-Enabled High-Performance Near-Infrared AgAuSe Quantum Dot Light-Emitting Diodes.

Near-infrared (NIR) quantum dot (QD) light-emitting diodes (LEDs) (NIR-QLEDs) for recognition and tracking applications underpin the future of night-vision technology. However, the performance of environmentally benign materials and devices has lagged far behind that of their Pb-containing counterparts. In this study, we demonstrate the superior performance of NIR-QLEDs based on efficient AgAuSe QDs with contact interface mediation. Consequently, we reveal that using cysteamine-treated QD film contact heterointerfaces can effectively eliminate contact defects in devices and preserve their excellent emissive properties. Additionally, the dipole moment orientation of the coordinated additives is inverse of the heterojunction potential difference, simultaneously blocking electrons and enhancing hole injection in operando, optimizing the LED charge injection balance. These devices exhibit a high external quantum efficiency (EQE) and a power conversion efficiency (PCE) of 15.8 and 12.7% at 1046 nm, respectively, a sub-band gap turn-on voltage of 0.9 V, and a low current density (over 10% of the EQE from 0.0017 to 0.31 mA cm ^-2 ). These are the highest EQE and PCE values ever reported for environmentally benign NIR-QLEDs. The results of this study can provide a general strategy for the practical application of QDs in electroluminescent devices.