Far-red-emitting double-perovskite CaLaMgSbO 6 :Mn 4+ phosphors with high photoluminescence efficiency and thermal stability for indoor plant cultivation LEDs.

A series of Mn ⁴⁺ -activated CaLaMgSbO ₆ far-red-emitting phosphors were synthesized by a solid-state reaction route and the microstructure and optical characterizations were investigated in detail. Upon excitation at 370 and 469 nm, the samples showed intense far-red emission at about 708 nm originating from the ² E _g → ⁴ A _2g transition and the optimal Mn ⁴⁺ concentration was 0.7 mol%. The as-prepared phosphors also exhibited excellent internal quantum efficiency (88%) and high thermal stability. The emission intensity at room temperature dropped to 54% when the temperature rose to 423 K and the activation energy was 0.34 eV. The outstanding optical properties and the fact that the emission band of the obtained phosphors had a broad overlap with the absorption band of phytochrome P _FR demonstrated that the CaLaMgSbO ₆ :Mn ⁴⁺ phosphors may be promising potential spectral converters for applying to indoor plant cultivation light-emitting diodes.
Competing Interests: There are no conflicts to declare.
(This journal is © The Royal Society of Chemistry.)