Thin film nanoarchitectonics of layer-by-layer assembly with reduced graphene oxide on intraocular lens for photothermal therapy of posterior capsular opacification.

Due to development of surgical techniques and intraocular lens (IOL) implants, vision can often be restored in cataracts patients. However, posterior capsular opacification (PCO) has become the most common and challenging complication in cataracts surgery. While various approaches such as surface modification and drug prophylaxis have been investigated to prevent PCO development, there is no standard treatment that is sufficiently safe and effective to meet clinical demands. Near-infrared (NIR) light-triggered photothermal therapy is an attractive noninvasive treatment for PCO prophylaxis. We fabricated a new type of IOL with excellent biocompatibility, stability, and photothermal conversion property. Polyethyleneimine (PEI) and graphene oxide (GO) were layer-by-layer assembled on model polymethylmethacrylate and IOL substrates, and the thickness, surface roughness, and wettability of the substrates with different numbers of bilayers were evaluated. After the reduction of GO to reduced GO (rGO), a rGO/PEI multilayer thin film with good stability and photothermal conversion capability was obtained. The rGO/PEI multilayer coating was able to induce apoptosis in lens epithelium cells under 808-nm NIR laser irradiation in vitro. Finally, rGO@IOL was implanted into rabbit eyes, and the biocompatibility and ability to prevent PCO were evaluated for 5 weeks. The rGO@IOL implant exhibited excellent PCO prevention ability with the assistance of NIR irradiation and did not induce obvious pathological effects in surrounding healthy tissues. The rGO@IOL implant with good biocompatibility, good physicochemical stability, and excellent photothermal conversion property shows promise for clinical application in PCO prophylaxis.
Competing Interests: Declaration of Competing Interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
(Copyright © 2022 Elsevier Inc. All rights reserved.)