Fabrication of Wettability-Patterned Surface for Cellular Micropatterning Using Step-Wise Ion Beam Processing.

In this study, the fabrication of a wettability patterned surface for cellular micropatterning was investigated using step-wise ion beam processing. A perfluorinated poly(ethylene-co-propylene) (FEP) film was first irradiated using accelerated Xe+ ions with 100 keV of energy at the low current density of 1 μ A/cm² over the entire surface. Second, its confined regions were irradiated at the higher current density of 15 μ A/cm² at various ion fluences through the pattern mask to generate patterns with big differences in wettability. From the analytic results, it was clearly verified that the step-wise irradiation induced effective chemical and morphological changes on the FEP surface, resulting in the successful formation of well-defined micropatterns with relatively hydrophilic and superhydrophobic surfaces. Moreover, the results of in-vitro cell culture showed well-resolved formation of 200 μ m cell micropatterns on the wettability patterned FEP surface due to the individual effects of the relatively hydrophilic and superhydrophobic properties on the cell adhesiveness and proliferation.