Effectiveness of implant surface debridement using particle beams at differing air pressures.

Because implant surface decontamination is challenging, air powder abrasive systems have been suggested as an alternative debridement method. This in vitro study investigated the effectiveness of different powder formulations and air pressures in cleaning implant surfaces and the extent of surface damage. A validated ink model of implant biofilm was used. Sterile 4.1 × 10 mm Grade 4 titanium implants were coated in a blue indelible ink to form a uniform, visually detectable biofilm-like layer over the implant threads and mounted into a bone replica material with bony defects to approximate peri-implantitis. Air powder abrasive treatments were undertaken using glycine, sodium bicarbonate, or calcium carbonate powder at air pressures of 25, 35, 45, and 55 psi. Digital macro photographs of the threads were stitched to give composite images of the threads, so the amount of ink remaining could be quantified as the residual area and expressed as a percentage. Implant surfaces were also examined with scanning electron microscopy to grade the surface changes. No treatment cleaned all the surface of the threads. The powders were ranked in order of decreasing effectiveness and decreasing surface change into the same sequence of calcium carbonate followed by sodium bicarbonate followed by glycine. Higher air pressure improved cleaning and increased surface change, with a plateau effect evident. All powders caused some level of surface alteration, with rounding of surface projections most evident. With air powder abrasive systems, there is a trade-off between cleaning efficacy and surface damage. Using this laboratory model, sodium bicarbonate and calcium carbonate powders were the most effective for surface cleaning when used at air pressures as low as 25 psi.