Chemical tracer diffusion of Sr and Co in polycrystalline Ca-deficient CaMnO 3-δ with CaMn 2 O 4 precipitates.

Diffusivity on the A- and B-site of polycrystalline perovskite CaMnO _3-δ with Ca deficiency and spinel CaMn ₂ O ₄ (marokite) as a secondary phase was studied using chemical tracers and secondary ion mass spectrometry (SIMS) complemented by electron probe microanalysis (EPMA). Thin films containing Sr and Co chemical tracers were deposited on the polished surface of the polycrystalline composite sample followed by annealing at 800-1200 °C for 96 h. Diffusion profiles for each tracer were determined with SIMS, followed by calculation of diffusion coefficients by fitting to appropriate models. The Sr tracer showed mainly lattice diffusion, with an activation energy of 210 ± 30 kJ mol ^-1 , whereas the Co tracer showed a combination of lattice and enhanced grain-boundary diffusion, with activation energies of 270 ± 30 kJ mol ^-1 and 380 ± 40 kJ mol ^-1 , respectively. The diffusivities may be used to predict interdiffusion and lifetime of junctions between n-type CaMnO _3-δ or CaMnO _3-δ /CaMn ₂ O ₄ composites and metallization interlayers or p-type leg materials in oxide thermoelectrics. In particular, the relatively high effective diffusivity of Co in polycrystalline CaMnO _3-δ may play a role in the reported fast formation of the secondary phase (Ca ₃ Co _2-y Mn _y O ₆ ) between p-type Ca ₃ Co _3.92 O _9+δ and n-type CaMnO _3-δ in a direct p-n thermoelectric junction.