Zn-Li alloy after extrusion and drawing: Structural, mechanical characterization, and biodegradation in abdominal aorta of rat.

Zinc shows great promise as a bio-degradable metal. Our early in vivo investigations implanting pure zinc wires into the abdominal aorta of Sprague-Dawley rats revealed that metallic zinc does not promote restenotic responses and may suppress the activities of inflammatory and smooth muscle cells. However, the low tensile strength of zinc remains a major concern. A cast billet of the Zn-Li alloy was produced in a vacuum induction caster under argon atmosphere, followed by a wire drawing process. Two phases of the binary alloy identified by x-ray diffraction include the zinc phase and intermetallic LiZn ₄ phase. Mechanical testing proved that incorporating 0.1wt% of Li into Zn increased its ultimate tensile strength from 116±13MPa (pure Zn) to 274±61MPa while the ductility was held at 17±7%. Implantation of 10mm Zn-Li wire segments into abdominal aorta of rats revealed an excellent biocompatibility of this material in the arterial environment. The biodegradation rate for Zn-Li was found to be about 0.008mm/yr and 0.045mm/yr at 2 and 12months, respectively.
(Copyright © 2017 Elsevier B.V. All rights reserved.)