[Studies on bond strength and hardness of base materials].

Since base materials are used in the construction of abutment teeth and the cavity walls of the teeth with healthy pulp, they need considerable bonding and mechanical strength depending on the site of application. In the present study we examined bonding strength, Martens-Mayer hardness and Vickers hardness of base materials in comparison with natural dentin in order to reevaluate them in terms of prosthetic materials and to provide assessment criteria for their application to prosthetic treatment. The results were as follows: 1) The bonding test showed the lowest value (4.6kgf/cm2) in calcium hydroxide FR (HFR) and the highest (47.9kgf/cm2) in HY-Bond polycarboxylate cement (CHC), a type of polycarboxylate cement. 2) In the test of bonding strength with various types of cement, calcium hydroxide preparations and zinc phosphate cement showed low values (4.6-23.5kgf/cm2) while polycarboxylate cement and glass-ionomer cement showed relatively high values (17.8-40.5kgf/cm2). 3) The Martens-Mayer hardness test showed the highest value (10.82 x 10(4] in dentin cement (GDE) and the lowest (1.09 x 10(4] in propack (EPR). 4) The Vickers hardness test showed the highest value (82) in neo-protect cement (ZPR) and the lowest (1) in propack (EPR). 5) In both Martens-Mayer and Vickers hardness tests with various types of cement, zinc phosphate cement and glass- ionomer cement showed high values, while low values were obtained in calcium hydroxide preparations and zinc-oxide eugenol cement. 6) Zinc phosphate cement and glass-ionomer cement showed no statistically significant differences from natural dentin in either Martens-Mayer hardness or Vickers hardness.