Effects of nano-TiC p on the microstructures and tensile properties of TiC p /Al–Cu composites.
- Source :
-
Materials Characterization . Aug2014, Vol. 94, p80-85. 6p. - Publication Year :
- 2014
-
Abstract
- Abstract: Many experimental and theoretical studies indicated that the decrease of the size of the reinforcing particles can lead to substantial improvements in the mechanical performance of the composites. However, the investigations on the addition of the nano particles into conventional metal materials are still rare, especially the nano-TiC p into the Al–Cu alloys. In this study, the Ni coated nano-TiC p reinforced Al–Cu matrix composites were successfully fabricated by a casting route. It was found that the nano-TiC p was in the α-Al grains. The α-Al dendrites became finer and more developed. Moreover, the θ′ precipitates in the Al–Cu matrix were finer and uniformly distributed. The tensile strength and elongation of the composites increased simultaneously. After T6 heat treatment, compared with the unreinforced Al–Cu alloy, the tensile strength and elongation of the 0.8wt.% nano-sized TiC p /Al–Cu composite increased from 485MPa and 6.6% to 573MPa and 12.4%, respectively. [Copyright &y& Elsevier]
Details
- Language :
- English
- ISSN :
- 10445803
- Volume :
- 94
- Database :
- Academic Search Index
- Journal :
- Materials Characterization
- Publication Type :
- Academic Journal
- Accession number :
- 96787176
- Full Text :
- https://doi.org/10.1016/j.matchar.2014.05.012