Curing and thermal behaviour of a flame retardant cycloaliphatic epoxy resin based on phosphorus containing poly(amide-imide)s.
- Source :
-
Journal of Thermal Analysis & Calorimetry . Feb2014, Vol. 115 Issue 2, p1693-1703. 11p. - Publication Year :
- 2014
-
Abstract
- The curing behaviour of 3,4-epoxycyclohexylmethyl 3,4-epoxycyclohexane carboxylate was investigated by the dynamic differential scanning calorimetry (DSC) using phosphorus-containing poly(amide-imide)s (PAIs) having free amine groups, 4,4′-diaminodiphenylmethane (PM) and p-phenylenediamine (PA), in the ratio of 1:1. The PAIs were prepared by co-polymerization of diimide-diacid (DIDA) and phosphorus-containing triamines having phenylene moiety. l-Tryptophan and pyromellitic anhydride were used to synthesize DIDA. Triamines used in the synthesis PAIs were tris(3-aminophenyl) phosphine (TAP), tris(3-aminophenyl) phosphine oxide (TAPO) and bis(3-aminophenyl) aminotolyl phosphine (BAP). TAP-, TAPO- and BAP-containing PAIs were designated as PTAP, PTAPO and PBAP, respectively. These PAIs with free amine groups were characterized by FTIR, H NMR, C NMR spectroscopic techniques and elemental analysis. The mixture of PAIs and PM or/and PA in the ratios of 0:1, 1:0 and 0.5:0.5 was used for investigation. DSC was used to study the curing of epoxy by recording the DSC scans at heating rates of 10 °C min. Thermal stability of epoxy resin cured isothermally was evaluated by recording thermo gravimetric traces in nitrogen atmosphere at the heating rate of 20 °C min. All samples are highly stable, and the 10 % mass loss found was in the range of 335-520 °C. The percent char yield was highest in case of resin sample E/PM/PTAPO. The flame-retardant properties of cured epoxy resins were investigated by the limiting oxygen index test (LOI) and UL94 test. When phosphorus was incorporated in epoxy resin, the epoxy resin system met the UL94 V-0 classification and the LOI reached at 37.8, because of nitrogen-phosphorus synergistic effect. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 13886150
- Volume :
- 115
- Issue :
- 2
- Database :
- Academic Search Index
- Journal :
- Journal of Thermal Analysis & Calorimetry
- Publication Type :
- Academic Journal
- Accession number :
- 93752778
- Full Text :
- https://doi.org/10.1007/s10973-013-3391-x