Thermodynamic studies of CaLaFe11O19(s).
- Source :
-
Journal of Solid State Chemistry . May2013, Vol. 201, p68-74. 7p. - Publication Year :
- 2013
-
Abstract
- Thermodynamic studies on CaLaFe11O19(s) were carried out using Knudsen effusion mass spectrometry and calorimetry, viz. differential scanning calorimetry and high temperature oxide melt solution calorimetry. Standard molar Gibbs free energy of formation (Δ f G 0 m ), enthalpy of formation and heat capacity (C 0 p, m ) of the compound were calculated as a function of temperature for the first time. C 0 p, m (CaLaFe11O19) was determined and used for second law analysis, from which enthalpy and entropy of formation of the compound were calculated and the respective values are: Δ f H 0 m (298.15K)/kJmol−1=−6057(±8) and S 0 m (298.15K)/JK−1 mol−1=427(±5). Δ f H 0 m (298.15K)/kJmol−1: −6055(±6) was also calculated using oxide melt solution calorimetry, which is in close agreement with the second law value. A heat capacity anomaly was also observed at T=684K. A table of thermodynamic data from 298.15K to 1000K for CaLaFe11O19(s) was also constructed to represent an optimized set of data. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 00224596
- Volume :
- 201
- Database :
- Academic Search Index
- Journal :
- Journal of Solid State Chemistry
- Publication Type :
- Academic Journal
- Accession number :
- 89027029
- Full Text :
- https://doi.org/10.1016/j.jssc.2013.02.010