Rheological Behavior of Blends of Poly(Phenylene Sulfide) with a Thermotropic Liquid Crystalline Aromatic Poly(Ether Ester).

A new type of thermotropic liquid crystalline aromatic poly(ether ester) (PEE) was prepared from 1,3-bis(4′-carboxyphenoxy)benzene, 1,4-diacetoxybenzene, and p-acetoxybenzoic acid through a melt transesterification process. The rheological behavior of blends of poly(phenylene sulfide) (PPS) with PEE was studied using a high-pressure capillary rheometer with the shear rate range of 50 s−1 to 3000 s−1. The results show that according to the range of shear rate, the flow curves of PEE/PPS blends can be divided into three zones: a first shear-thinning zone (n < 1, “n” represents non-Newtonian indexes), a shear-thickening zone (n > 1), and a second shear-thinning zone (n < 1), and the former two zones are more obvious with the increase of PEE content or elevated temperature. In the second shear-thinning zone, the PPS melt is close to a Newtonian fluid at high temperature and high shear rate; meanwhile the non-Newtonian behavior of the PPS melt at high temperature is enhanced with the addition of PEE. The apparent viscosity of PPS melts sharply dropped after adding PEE, especially at relatively low temperature and low shear rate. The curve of apparent viscosity vs. shear rate starts to flatten out after adding PEE, suggesting that the addition of PEE lowers the sensitivity of PPS to shear rate. As the content of PEE increases, the activation energy of the viscous flow, ΔEη, of PPS decreases, which means that adding PEE weakens the temperature sensitivity of the apparent viscosity of the PPS melt. It can clearly be seen that the addition of PEE is beneficial to the processing of PPS. [ABSTRACT FROM AUTHOR]