Influence of Crystal Orientation on Magnetic Properties in 3% Silicon Steel With Ultra-High Tension TiN Coating.

The influence of the tile angle of the [001] out of crystal surface \beta on iron loss improvement of 3 % Si steel single crystals was investigated. This iron loss improvement was caused by tensile stress effect of TiN coating and domain refinement. When \beta angle was less than 3 degrees, both eddy current loss and hysteresis loss decrease. Extremely low iron loss was obtained, when \beta angle equal to about 2 degrees. On the other hand, when \beta angle is more than 3 degrees, the hysteresis loss increased though the eddy current loss decreased by TiN coating. As a result, change in iron loss was small after TiN coating and domain refining. Therefore, it was clarified that the iron loss improving methods, such as domain refining and ultra-high tension coating, were effective especially in grain oriented electrical steel whose \beta angle is less than 3 degrees. [ABSTRACT FROM PUBLISHER]