Hybrid Drying of Rubberwood Using Superheated Steam and Hot Air in a Pilot-Scale.

A pilot-scale rubberwood dryer was constructed and injected with superheated steam and hot air to study the effect of the hybrid system on the drying rate and mechanical properties of the wood. A total of 300 pieces of rubberwood boards, each with dimensions of 1000 mm long × 76.2 mm wide × 25.4 mm thick, were stacked in 1.0 m × 1.0 m × 1.7 m (1.7 m3) pallet. The stack was impinged with alternating cycles of superheated steam and hot air. The time required for conventional drying was 168 hours, but the drying time for the hybrid system was only 64 hours, resulting in a 62% reduction. After being dried, the rubberwood boards were mechanically tested for static bending, compression strength, hardness, and shear strengths. From the mechanical tests, the hybrid drying system using superheated steam and hot air had no significant effect on the mean shear strength parallel-to-grain; however; the mean compression strength parallel-to-grain was reduced by 24.2% and the mean MOR by 21.4%. Nonetheless, the mean MOE was increased by 30.4% and the mean of hardness by 16.4%. [ABSTRACT FROM AUTHOR]