Spectroscopic properties of Yb3+ and Er3+ ions in heavy metal glasses

Abstract: Selected heavy metal glasses containing Yb3+ and Er3+ ions have been studied. Near-infrared luminescence spectra at 1.53μm and up-conversion spectra of Er3+ ions were registered under excitation of Yb3+ ions by 975nm diode laser line. The luminescence bands correspond to 4I13/2–4I15/2 (NIR), 4S3/2–4I15/2 (green) and 4F9/2–4I15/2 (red) transitions of Er3+, respectively. The optical transitions of rare earth ions have been examined as a function of glass host. The unusual large spectral linewidth nearly close to 110nm for 4I13/2–4I15/2 transition of Er3+ ions in Yb–Er co-doped lead borate glass was obtained, whereas long-lived NIR luminescence at 1.53μm was detected in lead germanate glass. The NIR luminescence and up-conversion phenomena strongly depend on stretching vibrations of glass host, which was confirmed by FT-IR spectroscopy. [Copyright &y& Elsevier]