Piezoelectric and Dielectric Properties of Lead-Free (1-x)(Bi0.5K0.5)TiO3-xBiFeO3 Ceramics.

Dielectric and piezoelectric properties of lead-free (1-x)(Bi0.5K0.5)TiO3-xBiFeO3 ceramics prepared by a conventional solid-state reaction method were studied in the range of x = 0∼40 mol%. A tetragonal perovskite structure was maintained at x = 0∼10 mol% forming a solid solution between (Bi0.5K0.5)TiO3 and BiFeO3 with no secondary phase. Piezoelectric coefficient (d33) increased from 31 pC/N at x = 0 mol% to 64 pC/N at x = 6 mol% and then decreased with further addition of x. Depolarization temperature (Td) gradually decreased with increasing x from 302°C at x = 0 mol% to 163°C at x = 20 mol% and slightly increased up 180°C at x = 40 mol%. [ABSTRACT FROM AUTHOR]