Rapid densification and reaction sequences in self-reinforced Y-α-SiAlON ceramics with barium aluminosilicate as an additive

Abstract: Y-α-SiAlON (Y1/3Si10Al2ON15) ceramics with 5wt.%BaAl2Si2O8 (BAS) as an additive were synthesized by spark plasma sintering (SPS). The kinetic of densification, phase transformation sequences and grain growth during sintering process were investigated. Full densification could be achieved by 1600°C without holding and using a heating rate of 100°Cmin−1, but the transformation from α-Si3N4 to α-SiAlON is not completed simultaneously with the densification process. The equilibrium phase assemblage could be reached after SPS at 1800°C for 5min and the resultant material possesses self-reinforced microstructure with high hardness of 19.2GPa and fracture toughness of 6.8MPam1/2. The complete crystallization of BAS is beneficial to the high temperature mechanical properties. The obtained could maintain the room strength up to 1300°C. [Copyright &y& Elsevier]