Synthesis of Nano-Crystalline Magnetite by SHS Route.
- Source :
-
IEEE Transactions on Magnetics . Jun2009, Vol. 45 Issue 6, p2496-2498. 3p. 2 Charts, 6 Graphs. - Publication Year :
- 2009
-
Abstract
- Nano-crystalline magnetite powder has been prepared successfully by self-propagating high-temperature synthesis (SHS) reaction using Fe, Fe2O3 and sodium perchlorate as starting materials. The synthesized powder has been subjected to intense milling using a planetary ball mill up to 10 h. The effects of Fe/Fe2O3 molar ratio as well as the milling time on the powder particle characteristics were investigated using XRD, SEM, TEM and VSM techniques. XRD results showed that the non-stoichiometric molar ratio (2.5 Fe+0.5 Fe2O3) is more favorable to synthesize magnetite phase. The phase composition was not affected significantly by milling process while both mean particle and crystallite size were decreased. Mean crystallite size of magnetite reduced from 90 to 40 nm after 10 h milling Saturation magnetization (Ms) increased from 47.6 in non-milled sample to 69.6 emu/g in milled sample for 10 h, while the coercivity (Hc) reduced from 365 to 120 Oe after milling. [ABSTRACT FROM AUTHOR]
- Subjects :
- *NANOCRYSTALS
*MAGNETITE
*IRON ores
*OXIDE minerals
*FERROMAGNETISM
Subjects
Details
- Language :
- English
- ISSN :
- 00189464
- Volume :
- 45
- Issue :
- 6
- Database :
- Academic Search Index
- Journal :
- IEEE Transactions on Magnetics
- Publication Type :
- Academic Journal
- Accession number :
- 41534346
- Full Text :
- https://doi.org/10.1109/TMAG.2009.2018671