Effect of tin content and reduction temperature on the catalytic behaviour of PtSn/TiO2 catalysts in the vapour-phase hydrogenation of crotonaldehyde

Abstract: This paper reports a study of PtSn/TiO2 catalysts reduced at two different temperatures (473 and 773K) by infrared spectroscopy of CO adsorbed at 298K and XPS, as well as their behaviour in the vapour phase selective hydrogenation of crotonaldehyde at 333K. Catalysts with 2wt% Pt and different Pt:Sn atomic ratios were prepared by co-impregnation of a commercial TiO2 (P25, from Degussa) with aqueous solutions of H2PtCl6 and SnCl2·2H2O. XPS results show that tin is in oxidized state when the catalysts are reduced at 473K, whereas a proportion is in the metallic state after reduction at 773K. The amount of surface platinum decreases when the tin loading and the reduction temperature increase. The presence of Pt-Sn alloy in the catalysts after reduction at high temperature has been assessed by in situ IR spectroscopy of adsorbed CO, although a proportion of platinum remains in a non-alloyed state. The catalytic activity in the vapour-phase hydrogenation of crotonaldehyde increases after high temperature reduction, and the same behaviour is obtained with selectivity towards the hydrogenation of the carbonyl bond to yield the unsaturated alcohol, the best selectivity being obtained for the catalyst with the lowest Pt/Sn ratio. [Copyright &y& Elsevier]