Fabrication of damascene Cu wirings using solid acidic catalyst

Abstract: The copper damascene process is one of the most promising technologies for fabricating Cu wirings for electronic devices such as LSIs. In this research, the fabrication of damascene Cu wirings was conducted using solid acidic catalyst. When a Cu-plated wafer, whose oxide is a basic oxide is dipped into a mixture of oxidizing solution and acidic solution, surface atoms are ionized and etched off into the solution. However, because conventional nonelectrolytic etching does not have a reference surface, it is difficult to utilize for planarization. Therefore, a new nonelectrolytic machining method using a cation-exchange fabric instead of an acidic solution was developed. To be more precise, the planarization of a Cu-plated wafer was carried out by rubbing with the cation-exchange fabric in ozone water. Basically, this method exploits chemical reactions so that the physical properties of the workpiece surface are not deteriorated. Furthermore, this method uses no chemicals except for ozone water, which easily dissociates into water and oxygen molecules; thus, this method is a low-cost, environmentally friendly process. In this paper, as a preliminary experiment, the nonelectrolytic etching of a Cu sample using solutions of O3 and CO2 was carried out to inspect the dependence of the etching rate on [O3] and [H+]. The results indicate that the etching rate increased as [O3] and [H+] increased. When [H+] was high relative to [O3], a smooth etch-pit-free surface was achieved. Next, nonelectrolytic etching using a cation-exchange fabric was carried out, and properties similar to those in the case of etching using solutions were obtained. Finally, damascene Cu wirings were fabricated using ozone water and a cation-exchange catalyst. [Copyright &y& Elsevier]