The Evaluation of Sandwich Composite Materials with Vegetable Fibers in a Castor Oil Polyurethane Matrix with Their Faces and Honeycomb Core Made in a 3D Printer.

Sandwich panels are widely used in the naval and aerospace industries to withstand the normal tensile, compressive, and shear stresses associated with bending. The faces of sandwich composites are usually made of metals such as aluminum and, in some studies with composites, using a polymeric matrix, but there are no studies in the literature using a castor oil polyurethane matrix. The core of the panel must keep the faces apart and be rigid perpendicular to them. To begin the work, a study was carried out on the influence of alkaline treatment on sisal fibers to increase the fibers' adhesion to castor oil polyurethane. There are no relevant studies worldwide on the use of this resin and the adhesion of vegetable fibers to this polyurethane. In this work, a study was carried out through a three-point bending test of sandwich panels using faces of composite material with sisal fibers subjected to an alkaline treatment of 10% by weight of sodium hydroxide and an immersion time of 4 h in the dissolution, which was the best chemical treatment obtained initially in a castor oil polyurethane matrix. The honeycomb cores were made by 3D printer and in this study two different printing filament materials, PETG and PLA, and two different core heights were compared. As a result of a traction test, it was observed that sisal fibers with chemical treatment in a castor oil polyurethane matrix can be used in composites, although the stress levels obtained are 50% lower than the stresses obtained in other matrixes such as epoxy resin. The combination of sisal faces in a castor oil polyurethane matrix and honeycomb cores made in a 3D printer showed good properties, which allows the use of renewable, sustainable and less aggressive materials for the environment. In all tests, PETG was 21% to 32% stronger than PLA. Although there was no rupture in the test specimens, the PETG cores deformed 0.5% to 3.6% less than PLA. The composites with PLA were lighter, because the core density was 13.8% lower than the PETG cores. Increasing the height of the honeycomb increased its strength. [ABSTRACT FROM AUTHOR]