Research on mechanical property degradation model of equipment compartment floor under atmospheric corrosion condition.

AbstractA mechanical property degradation model of material fatigue life varying with stress level and corrosion time was developed in this study. An acidified NaCl solution was used to accelerate the corrosion of stainless-steel samples, and the relationship between laboratory-accelerated corrosion and atmospheric corrosion was established using corrosion thickness loss parameters. Based on the results of a pre-corroded fatigue test, lg<italic>N–S–T</italic> surface models and a modified version of Miner’s rule for calculating nonlinear mechanical damage accumulation were proposed. Taking a real part of a high-speed train as an example, critical operating mileages considering material fatigue performance degradation under corrosion conditions were calculated, which were consistent with failure mileages of the census results. [ABSTRACT FROM AUTHOR]