Charge storage mechanism and pseudocapacitance performance of NiO and Ce-doped NiO synthesized via modified combustion technique.

Supercapacitors, as promising energy storage devices, have gained significant attention due to their ability to deliver high power and efficient charge storage mechanisms. In this work, we report the synthesis and electrochemical characterization of pristine NiO and Ni 1-x Ce x O (x = 0.01, 0.02, 0.03) nanoparticles using a single-step auto ignition combustion method. Preliminary investigations indicate that Ni 1-x Ce x O (x = 0.02) nanoparticles (2 % Ce doping) exhibit superior specific capacitance compared to other compositions. Therefore, we focused on structural, morphological, and vibrational studies on pristine and 2 % Ce-doped NiO. XPS and BET techniques were explored to assess the electronic state and porosity of the samples. Subsequent electrochemical performance evaluations included Cyclic Voltammetry (CV) at various scan rates, Galvanostatic Charge-Discharge (GCD), and Electrochemical Impedance Spectroscopic (EIS) techniques. From CV at a scan rate of 5 mVs−1, specific capacitance values of 419 Fg-1 and 604 Fg-1 were obtained for pristine and 2 % Ce-doped NiO, respectively. GCD studies revealed a specific capacitance of 381 Fg-1 for 2 % Ce-doped NiO at a current density of 1 Ag-1 and demonstrated capacitance retention of 95.1 % over 3000 GCD cycles for a current density of 4 Ag-1. The symmetric two-electrode supercapacitor cell demonstrates exceptional electrochemical performance, exhibiting a high specific capacitance of 122 Fg-1, an impressive energy density of 8.17 WhKg−1, a power density of 700 WKg-1 at 1 Ag-1, and a remarkable 88 % capacitance retention after 5000 GCD cycles. DFT calculations suggest that Ce doping significantly alters pristine NiO's electronic and structural features due to lattice strain. Our work highlights the enhanced electrochemical performance of 2 % Ce-doped NiO and its potential as a good-quality supercapacitor material. [ABSTRACT FROM AUTHOR]