Effects of Process Parameters and Process Defects on the Flexural Fatigue Life of Ti-6Al-4V Fabricated by Laser Powder Bed Fusion.

The fatigue performance of laser powder bed fusion-fabricated Ti-6Al-4V alloy was investigated using four-point bending testing. Specifically, the effects of keyhole and lack-of-fusion porosities along with various surface roughness parameters, were evaluated in the context of pore circularity and size using 2D optical metallography. Surface roughness of Sa = 15 to 7 microns was examined by SEM, and the corresponding fatigue performance was found to vary by 102 cycles to failure. The S–N curves for the various defects were also correlated with process window examination in laser beam power–velocity (P–V) space. Basquin's stress-life relation was well fitted to the experimental S–N curves for various process parameters except keyhole porosity, indicating reduced importance for LPBF-fabricated Ti-6Al-4V alloy components. [ABSTRACT FROM AUTHOR]