Synthesis of praseodymium doped lutetium and gadolinium aluminum garnets modified by scandium and boron to improve luminescence properties.

The structural and luminescence properties of the Lu 3 Al 4 Sc 1 O 12 :Pr and Gd 3 Al 3 Sc 2 O 12 :Pr garnet scintillators co-doped with boron (B3+) ions were investigated. The addition of B3+ and Sc3+ to the structure has a positive effect on the luminescence properties, especially on the photo, radio emission intensities, quantum efficiency, and results in a reduction of the decay time, which is necessary for high-quality scintillators. Structural properties of garnets have been determined after X-ray diffraction analysis coupled with Rietveld refinement. Surface morphology analysis was performed using a scanning electron microscope and particle size was also determined. Elemental composition was confirmed by the ICP-OES technique. Reflection, excitation (in the UV and VUV range), emission (upon excitation by UV or X-rays), decay time, and quantum efficiency at room temperature were measured. Furthermore, the influence of temperature on excitation, emission, and decay curves was also analyzed. The obtained luminescence properties indicated positive effect caused by doping. [Display omitted] [ABSTRACT FROM AUTHOR]