The effect of MnO2 additive on the microstructure and mechanical properties of magnesium aluminate spinel.

In this study, varying amounts of MnO2 up to 5 wt.% were added to magnesium aluminate spinel (MA) bodies using a solid‐state sintering method at 1200–1600°C. The effect of MnO2 addition on the phase composition, microstructure, distribution of elements, and ionic valence of MA was investigated via X‐ray diffraction, scanning electron microscopy, energy‐dispersive spectroscopy, and X‐ray photoelectron spectroscopy, respectively. The results showed that Mg2+ ions in MA crystals were replaced by Mn2+ ions, resulting in the formation of the (Mg1‐<italic>x</italic>Mn<italic>x</italic>)Al2O4 solid solution. The distorted crystal structures promoted the sintering reactions, and the mechanical characteristics of MA were greatly improved by the solid solution strengthening process. When the additive amount of MnO2 was 5 wt.% and the sintered temperature reached at 1600°C, excess manganese ions hardly dissolved into the lattice of MA. And these ions were only distributed at the grain boundaries of MgAl2O4, forming a “barrier” that hindered the migration and diffusion of particles, thereby suppressing the sintering process and weakening the mechanical strength of MA. [ABSTRACT FROM AUTHOR]