Interfacial bond behavior of steel fibers embedded in manufactured sand-based ultra-high performance concrete.

The interfacial bond region between matrix and fibers is a non-negligible weak link that can significantly affect the mechanical properties of manufactured sand-based ultra-high-performance concrete (UHPMC). This study investigates the interfacial bond characteristics between steel fiber-UHPMC matrix using single-fiber pullout tests. Four variable parameters were considered: manufactured sand (MS) replacement ratio, stone powder content, fiber embedment length, and steel fiber geometry. Additionally, the microstructure of the steel fiber-UHPMC matrix interface was evaluated using backscattered electron microscopy (BSEM) and scanning electron microscopy (SEM). The results indicate that two typical failure modes including fiber pullout slip failure (in straight and hooked-end fibers) and fiber rupture failure (in corrugated fibers) were observed. The analysis of interfacial evaluation indicators shows that increasing the MS replacement ratio from 25 % to 100 % results in a decreasing trend in peak load, peak tensile stress, and energy consumption. Peak bond strength decreases with increasing embedment length. With the increase in stone powder content, the peak load, peak bond stress, and energy consumption increase initially and then decrease. Additionally, the interfacial failure mechanisms between straight/hooked-end steel fibers and the UHPMC matrix were further elucidated through bond-slip behavior characterization and microstructure analysis. Finally, a design-oriented bond-slip model was developed to predict the interfacial pull-out behavior of steel fiber -UHPMC matrix, showing favorable agreement between predicted and test results. These findings contribute to understanding the interfacial pullout behavior of steel fibers-UHPMC matrix, providing data reference for the performance optimization of UHPMC. • Interfacial bond characteristics of UHPMC are investigated by single-fiber pullout tests and BSEM/SEM techniques. • The stone powder content needs to be 4 % or higher to ensure good interfacial bond performance. • The pullout failure mechanisms of straight/hooked-end steel fibers from the UHPMC matrix were elucidated. • A design-oriented bond-slip model was developed to predict the pullout behavior between steel fiber and UHPMC matrix. [ABSTRACT FROM AUTHOR]