6082 铝合金的力学性能与热处理工艺的关系研究.

The continuous upgrading of the automobile industry has put forward higher requirements for the performance and lightweight effect of aluminum alloys. Heat treatment is an effective way to improve the performance of aluminum alloy, but how to obtain the optimal combination of heat treatment process parameters is an urgent problem. In this paper, the influence of heat treatment process parameters (solution temperature, solution time, aging temperature, aging time) on mechanical properties was systematically studied, and the relationship model between mechanical properties and heat treatment process parameters was established. The micromorphology under different process parameters were analyzed by ESDB and SEM. The results show that when the solution temperature was 530 ℃, the solution time was 1 h, the aging temperature was 170 ℃, and the aging time was 6 h, the mechanical property of 6082 aluminum alloy profiles was the best. The yield strength was 313 MPa, the tensile strength was 350 MPa, and the elongation after break was 13.21%. The relationship model between Y value (yield strength, tensile strength, and elongation after fracture) and key process factors was established, in which the solution temperature had the greatest influence. When the solution temperature was 530 ℃, the grain size was the smallest, and the mechanical properties of the precipitated fine Mg2Si phase and Al(FeMnSi) phase were the best, and the tensile fracture was mainly the dimpled fracture. This paper provides theoretical basis and practical guidance for the optimization of heat treatment process parameters of aluminum alloy profiles. [ABSTRACT FROM AUTHOR]