High photocatalytic degradation of methylene blue and enhancing the magnetization, AC conductivity of Dy3+ and Ce3+ doped CdCoFe2O4 nano ferrites.

Photocatalysts that combine with dielectric and magnetic properties are vital because of a wide variety of applications for these combinations, and nanostructured magnetic semiconductive materials have attracted significant interest due to their potential applications. A series of Cd 0.4 Co 0.6 Dy X Ce X Fe 2-2X O 4 spinel nano ferrites (nFs) were synthesized by using a highly efficient low-temperature method of citrate sol-gel auto-combustion for Methylene Blue (MB) dye degradation photocatalysts under visible light irradiation that combines with dielectric and magnetic properties are vital because of a wide variety of applications for these combinations, and nanostructured magnetic semiconductive materials have attracted significant interest due to their potential applications. The recycled MB is one of the hazardous textile dyes that is used extensively but causes risks for both humans and the environment. The prepared Dy3+ and Ce3+ doped Cd–Co nFs were polycrystalline with cubic structure, and crystalline size was increased from 15.78 to 21.02 nm with higher crystallinity, and the surface morphology changes from a spherical shape to a hexagonal shape with higher doping concentrations. The direct optical band gap values are increased. FTIR spectra reveal the stretching vibrations along the [M↔O] bond tetrahedral (A) and octahedral (B) sites. HRTEM results revealed that the prepared Cd–Co nFs have higher crystalline nature and high porosity. VSM indicates the sample's soft magnetic action and hysteresis loops showed the highest saturation magnetization (Ms) is 12.243 emu/g, and retentivity increases around 6.038 emu/g, decreasing the dielectric tangent loss, dielectric constant and dielectric loss. The AC conductivity raised with applied frequency. The PL gives a blue emission, and photocatalytic has the highest degradation activity 40.93 % of MB would be successful after 120 min irradiation of X = 0.07 Dy3+ and Ce3+ doped Cd–Co nFs. [Display omitted] [ABSTRACT FROM AUTHOR]