Upconversion, downshifting, quantum cutting and back energy trasfer from Yb3+ to Er3+ in Er3+/Yb3+ co-doped CaTiO3 phosphor, intense NIR generation for communication.

The perovskite based phosphor materials are widely used to increase the efficiency of solar cells. In this work, Er3+ doped and Er3+/Yb3+ co-doped CaTiO 3 perovskite phosphor samples have been synthesized by solid state reaction technique at 1473 K. The phosphor samples show orthorhombic phase with Pnma (62) space group. The average crystallites and particles size of CaTiO 3 are increased in presence of Er3+ and Yb3+ ions. Er3+ doped CaTiO 3 phosphor samples give downshifting emission under 379 nm excitation. Though upconversion emission is seen in Er3+ under 980 nm excitation without Yb3+ ions in this host. The emission intensity of Er3+ ion is enhanced by 46 and 16 times for green and red emissions, respectively in presence of Yb3+. An intense quantum cutting (QC) emission is observed at 980 nm in presence of Yb3+ in CaTiO 3 :0.5Er3+ phosphor under 379 nm excitation. The QC efficiency has been found to be 119 % for CaTiO 3 :0.5Er3+/5 Yb3+ phosphor. Further an interesting phenomenon of back energy transfer (BEnT) from Yb3+ to Er3+ giving an intense NIR emission from Er3+ at 1002 and 1550 nm have been observed. The phosphor sample also shows an intrinsic optical bistablity (IOB) by upconversion. Thus, the prepared phosphor samples may be useful to increase the efficiency of c-Si solar cell, NIR emission for communication, bistable material and green light emitting source. [Display omitted] [ABSTRACT FROM AUTHOR]