Stable Structure and Fast Ion Diffusion: A Flexible MoO 2 @Carbon Hollow Nanofiber Film as a Binder-Free Anode for Sodium-Ion Batteries with Superior Kinetics and Excellent Rate Capability.

Designing innovative anode materials that exhibit excellent ion diffusion kinetics, enhanced structural stability, and superior electrical conductivity is imperative for advancing the rapid charge–discharge performance and widespread application of sodium-ion batteries. Hollow-structured materials have received significant attention in electrode design due to their rapid ion diffusion kinetics. Building upon this, we present a high-performance, free-standing MoO2@hollow carbon nanofiber (MoO2@HCNF) electrode, fabricated through facile coaxial electrospinning and subsequent heat treatment. In comparison to MoO2@carbon nanofibers (MoO2@CNFs), the MoO2@HCNF electrode demonstrates superior rate capability, attributed to its larger specific surface area, its higher pseudocapacitance contribution, and the enhanced diffusion kinetics of sodium ions. The discharge capacities of the MoO2@HCNF (MoO2@CNF) electrode at current densities of 0.1, 0.2, 0.5, 1.0, 2.0 and 5.0 A g−1 are 195.55 (155.49), 180.98 (135.20), 163.81 (109.71), 144.05 (90.46), 121.16 (71.21) and 88.90 (44.68) mAh g−1, respectively. Additionally, the diffusion coefficients of sodium ions in the MoO2@HCNFs are 8.74 × 10−12 to 1.37 × 10−12 cm2 s−1, which surpass those of the MoO2@CNFs (6.49 × 10−12 to 9.30 × 10−13 cm2 s−1) during the discharging process. In addition, these prepared electrode materials exhibit outstanding flexibility, which is crucial to the power storage industry and smart wearable devices. [ABSTRACT FROM AUTHOR]