Wet H2S corrosion and degradation of pipeline in amine regeneration system.

The paper presents the results of non‐destructive testing examinations, metallographic tests and risk assessment of degradation related to corrosion of amine regeneration unit in a desulphurisation system. Intensive corrosion resulting from acid gases environment upon water condensation causes perforation of the pipeline. Detailed analysis reveals cracking related to the mechanism of wet H2S. Hydrogen penetration, resulting from the wet H2S process, causes a decrease in mechanical properties of steel and an increase in hydrogen content inside steel. Corrosion results mostly from high stream velocity, the presence of acid gases (with high ammonia content), the presence of amine and low stream temperature. [ABSTRACT FROM AUTHOR]