Microstructure and Properiies of the Recycled A-1. 15Mg-1. 02S-0. 7Cu Alloy with High Strength and Toughness.

:In paper, recycled Al-1.15Mg-1.02Si-0.7Cu alloy was optical prepared by meiting and casting, the microstructural evolution of the alloy were analyzed by using optical nicroscopy(OM), scanning e!ectron microscopy (SEM), e!ectron back scattered diffraciion(EBSD) and transmission e!ectron nicroscope(TEM),the effects of heal treatment on the mechanical and corrosionlresistant properties of the extruded proUes were invesiigated. The results show that the recrystaliization of the alloy was competed by soiid solution at 550C and fine equaaxaal crystass were obtanned. The iime required for the alloys to reach peak hardness under artificia1 aging cond!tions at 155,175 and 195 C was 18,8 and 4 h, respectively, and the peak hardnesses were 132.96 HV,132. 94 HV and 132.22 HV, respectively, wtth the extruded profiles obtanning the highest tensle strength of 410. 42 MPa and higher elongation of 14. 75% under aging cond!tions at 175 C/8 h. The optimizedsoid solution process ss 550 C/1 hand the artifidal aging process ss 175 C/8 h. The tendency of the alloy to intergranular corrosion ss more pronounced,and the alloy corrodes most severely under peakaged cond!tions, followed by over-aged and weakest underaged. [ABSTRACT FROM AUTHOR]