Mechanical Properties of High- and Low-Fusing Zirconia Veneering Ceramics Fired on Different Trays and Substrates.

This study aimed to evaluate the effect of ceramic type, firing tray, and firing substrate on the density, shrinkage, biaxial flexural strength, Martens' hardness, and elastic indentation modulus of zirconia veneering ceramics. Disk-shaped specimens were fabricated from a high-fusing (HFZ) and a low-fusing (STR) zirconia veneering ceramic. These specimens were then divided into 10 groups according to firing trays (round, small honeycomb-shaped, cordierite [RSC]; round, large honeycomb-shaped, aluminum oxide [RLA]; rectangular, plane, silicon nitride [RCPS]; round, plane, silicon nitride [RPS]; and rectangular, plane, calcium silicate [RCPC]) and firing substrates (firing cotton and platinum foil) used (n = 12). The density, shrinkage, biaxial flexural strength, Martens' hardness, and indentation modulus were measured, and analyzed with generalized linear model analysis (α = 0.05). The interaction between the ceramic type and firing substrate affected density (p < 0.001), and the other outcomes were affected by the interaction among all main factors (p ≤ 0.045). Higher density was observed with HFZ or platinum foil (p ≤ 0.007). RSC and RLA led to a higher density than RCPS within HFZ and led to the lowest density within STR (p ≤ 0.046). STR had a higher shrinkage (p < 0.001). RSC mostly led to a lower shrinkage of HFZ (p ≤ 0.045). The effect of ceramic type and firing substrates on the biaxial flexural strength, Martens' hardness, and indentation modulus was minimal while there was no clear trend on the effect of firing tray on these properties. Ceramic type, firing tray, and firing substrate affected the mechanical properties of the tested zirconia veneering ceramics. Firing the tested zirconia veneering ceramics over a round and small honeycomb-shaped cordierite firing tray with firing cotton mostly led to improved mechanical properties. [ABSTRACT FROM AUTHOR]