High-temperature synthesis of cast vanadium nitrides and aluminum oxynitrides.

This paper presents experimental results concerning the one-step preparation of cast divanadium nitride and aluminum oxynitride (AlON) by high-temperature synthesis under 5 MPa of N 2 from green mixtures containing vanadium oxide, aluminum, and aluminum nitride. It was shown that the mixtures with a wide range of component ratios are capable to burn with the temperature exceeding the melting point of the final products, divanadium nitride and aluminum oxynitride, that makes it possible to obtain them in the form of a melt with subsequent separation of vanadium nitride (lower ingot) and aluminum oxynitride (upper ingot). The resulting products had no cohesion and were easily separated from each other. Variation in the content of aluminum nitride in the charge markedly affected the synthesis process, phase composition, and microstructure of the target products. The content of excess aluminum nitride in the starting mixture α = 10% was found to be optimum on a yield/composition of the target products. [ABSTRACT FROM AUTHOR]