Effect of T6 and T6I4 Aging Treatments on Microstructure and Compressive Properties of Aluminum Metal Matrix Composites Reinforced by SiCw Via Squeeze Casting.
- Source :
-
Metal Science & Heat Treatment . Mar2024, Vol. 65 Issue 11/12, p781-789. 9p. - Publication Year :
- 2024
-
Abstract
- The microstructure and compressive properties of the 7xxx series aluminum alloy (Al – 12.44Zn – 3.22Mg – 1.13Cu – 0.19Zr – 0.12Sr) reinforced with SiC whiskers via squeeze casting are investigated after aging treatments T6-1, T6-2, T6I4-1, and T6I4-2. For this purpose, the effect of four kinds of aging heat treatments on the properties of the aluminum metal matrix composites (AMMCs) is studied systematically through Vickers hardness and room temperature compressive testing. The microstructure is analyzed by optical microscopy, scanning electron microscopy, and x-ray diffraction. The experimental results show that the hardness of the AMMCs after four kinds of aging processes has different degrees of improvement compared to no-aging. After the T6-1, T6-2, T6I4-1, and T6I4-2 aging processes, the hardness of the composites is 325, 278, 306, and 345.8 HV, respectively. The additional T6-2 aging treatment provides the highest compressive strength and compressive strain, about 747 MPa and 7%, respectively, as well as a maximum dislocation strengthening of approximately 86.89 MPa. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 00260673
- Volume :
- 65
- Issue :
- 11/12
- Database :
- Academic Search Index
- Journal :
- Metal Science & Heat Treatment
- Publication Type :
- Academic Journal
- Accession number :
- 176803947
- Full Text :
- https://doi.org/10.1007/s11041-024-01006-4