Negative permittivity and permeability behaviour of SrFe12O19/rGO metacomposite for microwave absorption in 2–18 GHz range.

Double-negative performance has played a significant role in electronic applications owing to its both permeability and permittivity negative values. Microwave absorption material has a substantial role in electromagnetic shielding, radar absorption, stealth applications, etc. Herein, a novel double-negative metacomposite, SrFe 12 O 19 /rGO, was designed by a simple one-pot hydrothermal method, and the microwave absorption properties of the material were studied in the microwave region from 2 to 18 GHz using VNA analysis. The structural and morphological studies were analysed using XRD, FT-IR, and SEM instrumentation techniques and the magnetic property of the material was studied using VSM analysis. Both studies confirmed the hard magnetic nature of the material. The particle sizes of SrFe 12 O 19 and SrFe 12 O 19 /rGO measured from XRD are 55.60 nm and 41.55 nm, respectively. Hexagonal plate-like morphology were observed from FESEM images. The coercivity of SrFe 12 O 19 /rGO increased, and the magnetocrystalline anisotropy was changed due to the decrease in particle size. The magnetic saturation value decreases due to the presence of non-magnetic rGO. The resultant SrFe 12 O 19 /rGO metacomposite shows negative permittivity and permeability values. The minimum reflection loss values observed for pure and rGO-decorated strontium ferrites are −28.49 dB at 7.76 GHz and −23.78 at 11.04 GHz, respectively. In addition to experimental results, simulation studies were also performed to study the reflection loss with matching thickness using a quarter wavelength mechanism. The results show that this composite can be employed as a left-handed metamaterial that finds applications in absorption, antennas, sensors, wireless power transfer systems, etc. The left-handed metamaterial can shift the frequency region from a lower to a higher frequency region. The rGO decorated metacomposite is a promising material for microwave absorption at higher frequency regions. [ABSTRACT FROM AUTHOR]