Wet ball milling and hot press for the preparation of UHMWPE/modified MWCNTs nanocomposite with enhanced mechanical and thermal properties.
- Source :
-
Polymer Bulletin . Feb2024, Vol. 81 Issue 2, p1707-1727. 21p. - Publication Year :
- 2024
-
Abstract
- In this study, wet ball milling and hot press methods were used to prepare nanocomposite from ultra-high molecular weight polyethylene (UHMWPE) as a matrix, and modified multi wall carbon nanotubes (MWCNTs) as reinforcement nano-additives. Two batches of MWCNTs were used (Pristine-MWCNTs-B1, and Pristine-MWCNTs-B2). First, the MWCNTs were oxidized (oxide-MWCNTs) by wet chemistry using strong acids, then further functionalized with an amide group (A-MWCNTs). Fourier-transform infrared spectroscopy (FTIR), and Thermal gravimetric analysis (TGA) results confirm the functionalization of the MWCNT with the amide group. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) were used to examine the surface morphology and crystalline behavior of MWCNT after functionalization. Ball milling was used to mix the UHMWPE with pristine MWCNT (1.5% wt), Oxide-MWCNT (1.5% wt), and A-MWCNTs (0.5–2% wt). Then, hot press melting was used to prepare the nanocomposite sheets. Fourier transform infrared spectroscopy (FTIR) confirmed the impact of the balls milling process with time factor on UHMWPE crystallinity and the interaction of the functionalization MWCNT with the UHMWPE matrix. The structure (crystallinity, crystal size) was validated using X-ray diffraction (XRD) patterns. Thermal gravimetric analysis (TGA), differential scanning calorimeter (DSC), and universal testing machine (UTM) were utilized to analyze the structural, thermal, and mechanical properties of the nanocomposites, respectively. The results showed that UHMWPE crystallinity increased after 2 h of ball milling, while crystallinity decreased when pristine-MWCNT, oxide-MWCNTs, and A-MWCNTs (0.5–2 wt%) were added without affecting the crystal structure of UHMWPE. The results showed that adding 1.5 wt% A-MWCNTs-(B1, B2)/UHMWPE increased thermal stability by 16 °C and elongation at the break by up to 74% when used 1.5 wt% A-MWCNT-B1 and 2 wt% A-MWCNT-B2. This shows that the ball milling methods and amide group improved the dispersion and interface interaction between MWCNTs and UHMWPE matrix. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 01700839
- Volume :
- 81
- Issue :
- 2
- Database :
- Academic Search Index
- Journal :
- Polymer Bulletin
- Publication Type :
- Academic Journal
- Accession number :
- 174644894
- Full Text :
- https://doi.org/10.1007/s00289-023-04790-w