'Spider-like' POSS in NIPU webs: enhanced thermal stability and unique swelling behavior.

PEO-based non-isocyanate polyhydroxyurethane (NIPU, PHU) networks physically modified with octa(3-hydroxy-3-methylbutyldimethylsiloxy)POSS (8OHPOSS) were synthesized via one-pot one-step approach. POSS was introduced into the polymer matrix in the amount of 1–10 wt%. Polar hydroxyls on the vertex groups of POSS allowed for uniform dispersion even up to high loadings (10 wt%). Composites exhibit enhanced thermal stability in comparison to the pristine matrix. FTIR analysis confirmed that POSS strengthens the hydrogen bonding in the material. Upon POSS introduction, plasticization was observed with a peculiar trend change at POSS loadings over 5 wt%. Glass transition temperature of highly crystalline 8OHPOSS was measured and reported to be at around 3 °C. NIPUs at hand exhibit high water absorption (around 200 wt%) typical for hydrogels. Swelling studies show that 8OHPOSS enhances PHUs hydrogels absorption capacity in phosphate-buffered saline (PBS). Higher absorption capacity in PBS solution in comparison to distilled water is an uncommon phenomenon in hydrogels. [ABSTRACT FROM AUTHOR]