Synthesis of a novel siloxane-based crosslink agent and its application in emulsion copolymerization of butyl acrylate and methyl methacrylate.

Authors :
Yakdel, Mahmood
Zohuri, Gholam Hossein
Arabi, Seyed Mahmood
Hosseinpour, Pedram
Source :
Journal of Polymer Research. Nov2023, Vol. 30 Issue 11, p1-14. 14p.
Publication Year :
2023

Abstract

Improving water-based polymer's properties using silicon compounds is strongly noticed nowadays. A novel siloxane-based crosslink agent was synthesized using oligomeric polydimethylsiloxane (PDMS) hydroxyl-terminated. The crosslinker was used for emulsion copolymerization of methyl methacrylate (MMA), butyl acrylate (BA), and acrylic acid (AA). Incorporation of the crosslinker in the structure of the copolymer increased the average latex particle size (from about 165 to 207 nm) and as a result, the viscosity of the latexes was dramatically decreased (from 212 cP to 83 cP). The crosslink density of the latexes, meanwhile, was raised (from about 7–60%). Electrostatic stability of the latexes was improved in the presence of the crosslinker (zeta potential from − 31.7 mV to -49.5 mV and the average mobility of the latexes particles from − 2.4 μm/s/V/cm to -3.8 μm/s/V/cm). The crosslinking agent affected both the initial decomposition temperature and residual weight fraction of the copolymer (from 353 to 406 °C and from about 0.5 w% to 12.4 w% respectively). A morphological study of the latexes was carried out using transmission electron microscopy (TEM), scanning electron microscopy (SEM), and atomic force microscopy (AFM) techniques. The addition of the crosslinker, led to a decrease in the contact angle (from 70 to 39 degrees) of the latexes film formed. [ABSTRACT FROM AUTHOR]

Details

Language :
English
ISSN :
10229760
Volume :
30
Issue :
11
Database :
Academic Search Index
Journal :
Journal of Polymer Research
Publication Type :
Academic Journal
Accession number :
173822974
Full Text :
https://doi.org/10.1007/s10965-023-03807-2