Effect of Ni substitution on magnetic properties and microwave absorption of the Y2Co17 compounds and composites.

The rare earth alloy Y 2 Co 17 − x Ni x was prepared by a low-cost co-precipitation reduction-diffusion process, and its crystal structure, static magnetic properties, and microscopic morphology were systematically characterized. The effects of Ni doping with different contents on the electromagnetic parameters and wave absorption properties of Y 2 Co 17 − x Ni x /polyurethane(PU) compounds were researched in the frequency range of 0.1–18 GHz. The results show that the static magnetic properties and wave absorption properties change significantly with Ni doping, and the maximum reflection loss of Y 2 Co 14 Ni 3 /PU reaches − 89.7 dB at 2.9 mm thickness, and the maximum reflection loss peaks of Y 2 Co 17 /PU and Y 2 Co 16 Ni 1 /PU are at 1.316 and 1.515 GHz, which is at the center frequency of the L-band. With Ni doping, the effective absorption bandwidth of the compounds at a frequency above 3 GHz is greatly increased. The physical factor in the bandwidth calculation was modified, and the effective absorption bandwidth of the material was calculated theoretically, and the error was less than 5 % compared with the experimental value. [ABSTRACT FROM AUTHOR]