The effect of plasma treatment on the mode II interlaminar fracture toughness of Glass/Epoxy laminates.
- Source :
-
Theoretical & Applied Fracture Mechanics . Oct2023, Vol. 127, pN.PAG-N.PAG. 1p. - Publication Year :
- 2023
-
Abstract
- • The effect of plasma treatment on the mode II interlaminar fracture toughness of glass/epoxy laminates was studied experimentally. • Glass fiber layers at the top and bottom faces of the pre-delamination were treated by a dielectric-barrier discharge (DBD) plasma. • G IIC of glass/epoxy specimens was determined by subjecting end-notched bending (ENF) specimens to a 3-point-bending load. • Plasma treatment increased the G IIC of the specimens by ∼ 50%. • Fourier-transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM) methods were used to investigate the toughing mechanisms. Despite the key advantages of fiber-reinforced polymer composites, such as high specific strength and stiffness, these materials are characterized by low interlaminar fracture toughness. This study aims to investigate the effect of dielectric-barrier discharge (DBD) plasma treatment of glass fibers on the mode II interlaminar fracture toughness (G IIC) of glass/epoxy composite laminates. To this aim, first, end-notched bending (ENF) specimens were fabricated using the vacuum infusion process. During the laminating process of the specimens, the two adjacent glass layers at the top and bottom faces of the pre-delamination were exposed to an atmospheric DBD plasma for different exposure times (R: reference specimens without plasma treatment, PT2: specimens with two rounds of treatment, and PT5: specimens with five rounds of treatment). Afterward, the ENF specimens were subjected to three-point bending loading according to ASTM D7905 standard. The results showed an increase of ∼ 51% and ∼ 56% in G IIC for PT2 and PT5 specimens compared to the reference specimens (R), respectively. The Fourier-transform infrared spectroscopy (FTIR) analysis indicated that the plasma treatment did not generate new functional groups at the surface of glass fibers; therefore, there was no increase in the chemical bonding strength of the fibers to the resin. However, scanning electron microscopy (SEM) revealed that the plasma treatment increased the adhesion of the glass fibers to epoxy by removing sizing of the glass fibers and increasing the surface roughness of the fibers. The results of the present study showed that the plasma treatment can be considered as a cheap, easy-to-use, cost effective and scalable method for toughening laminated composites instead of the costly and difficult methods such as electrospun nanofibers and z-pinning. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 01678442
- Volume :
- 127
- Database :
- Academic Search Index
- Journal :
- Theoretical & Applied Fracture Mechanics
- Publication Type :
- Academic Journal
- Accession number :
- 173155574
- Full Text :
- https://doi.org/10.1016/j.tafmec.2023.104093