Luminescence and mechanoluminescence of Ba4Si6O16:Eu2+, RE phosphors.

The luminescence properties of green Ba4Si6O16:Eu2+, rare-earths (RE) (RE = Sc, Y, La and Lu except Pm) phosphors are reported. Their long-lasting phosphorescence is discussed in view of trap depths and concentrations determined from thermally stimulated luminescence experiments. A second emission band centered at 439 nm was evidenced at low temperatures, which stems from the substitution of Eu2+ in the two non-equivalent Ba2+ sites of Ba4Si6O16. The mechanoluminescence properties of Ba4Si6O16:Eu2+, RE phosphors are described, and a new mechanoluminescence mechanism is proposed, in the case where RE = Ho3+, involving a trap distribution from 0.694 to 0.924 eV. Mechanical loading (post UV irradiation) induces a decrease in depth of the trap distribution, leading to an increase of the luminescence intensity, whereas a drop of the luminescence intensity is observed upon unloading, following the faster release of the charge carriers. [ABSTRACT FROM AUTHOR]