Composition-mediated abnormal phase evolution in Ta-W films with Cr buffer layers.

With the monotonically increasing of W from 0 to 20 at. % in Ta-W films with Cr buffers, an abnormal phase evolution of α-Ta→β-Ta→α-Ta was found, which is due to the breaking and rebuilding of α-Ta nucleation. A small amount of W addition could disturb the epitaxial growth of α-Ta on Cr layers by refining the nucleus size. Nevertheless, as a completely miscible system, Ta-W solid solutions are preferred to possess the α-Ta structure. With the increasing W content, the nucleation barrier of α-Ta is correspondingly lower, facilitating the rebuilding of α-Ta growth. The effect of phase evolution competes with that of solid solution strengthening in the controlling mechanism of Ta-W hardness. The hardness of the sample with low W contents is largely influenced by the proportion of β-Ta, while the solid solution strengthening effect is more pronounced in high W. [Display omitted] [ABSTRACT FROM AUTHOR]