Transmission Electron Microscopy Peeled Surface Defect of Perovskite Quantum Dots to Improve Crystal Structure.

Transmission electron microscopy (TEM) is an excellent characterization method to analyze the size, morphology, crystalline state, and microstructure of perovskite quantum dots (PeQDs). Nevertheless, the electron beam of TEM as an illumination source provides high energy, which causes morphological variation (fusion and melting) and recession of the crystalline structure in low radiolysis tolerance specimens. Hence, a novel and facile strategy is proposed: electron beam peel [PbBr6]4− octahedron defects from the surface of QDs to optimize the crystal structure. TEM and high-angle annular dark-field scanning TEM (HAADF) tests indicate that the [PbBr6]4− octahedron would be peeled from the surface of QDs when QDs samples were irradiated under high-power irradiation, and then a clear image would be obtained. To avoid interference from a protective film of "carbon deposits" on the surface of the sample when using high resolution TEM, amorphous carbon film (15–20 nm) was deposited on the surface of QDs film and then characterized by TEM and HAADF. The detection consequences showed that the defection of PbBr2 on the surface of QDs will gradually disappear with the extension of radiation time, which further verifies the conjecture. [ABSTRACT FROM AUTHOR]