High photocurrent performance of nebulizer sprayed Bi2S3 thin films by a novel Cu-La doping strategy.

[Display omitted] • This research work pristine Bi 2 S 3 , Bi 2 S 3 :Cu2%, Bi 2 S 3 :La2%, and Bi 2 S 3 :Cu2%:La2% thin films were prepared by nebulizer spray pyrolysis. • The morphological studies using FESEM analysis showed the unformed distribution of small grains. • The optical absorbance spectra of the thin films were observed from the wavelength of 350 nm to 1000 nm. • films were subjected to analyzing U.V. photosensing properties. As a result, maximum responsivity (1.24 × 10−01 AW−1), detectivity (1.13 × 1010 Jones), and EQE (40%) were achieved for Bi 2 S 3 :Cu: La-sample. Nowadays, chalcogenide-based thin layers are proving a promising light-absorbing material with low cost and are technologically suitable for light to current conversion applications. In this study, for the first time, pristine Bi 2 S 3 , Bi 2 S 3 :Cu2%, Bi 2 S 3 :La2%, and Bi 2 S 3 :Cu2%:La2% thin films were prepared by nebulizer spray pyrolysis technique on a glass substrate at 300 °C. The obtained XRD pattern confirms the orthorhombic structure of Bi 2 S 3 and possesses a maximum crystallite size of 38 nm for Bi 2 S 3 :Cu: La co-doped sample. Images taken with a FESEM analysis showed the unformed distribution of round shaped grains without any cracks and co-doping leads to the development of slight cluster formation. The optical absorbance spectra of the thin films were observed from the wavelength of 350 nm to 1000 nm, and the co doping process highly strengthen the optical absorbance, which is prerequisite for an efficient photodetector. A lower band gap value of 1.7 eV is achieved for Bi 2 S 3 : Cu: La thin film. From PL studies, defect emission bands around ∼325 and 525 nm related to band edge emission and sulfur vacancies are obtained. Further, UV photosensing properties of each sample were evaluated. Commendable performance with maximum responsivity (1.24 × 10−1 AW−1), detectivity (1.13 × 1010 Jones), and EQE (40%) were achieved for Bi 2 S 3 :Cu:La-sample. The enhanced figures-of-merit are attributed large crystalline size, good crystallinity, lower bandgap and crack free surface. The photo sensing results may widen the field of photosensing application. [ABSTRACT FROM AUTHOR]