Scintillation Properties and Irradiation Damage of Large Size BaF2:Y Scintillation Crystals Grown by Bridgman Method.

The 40 mm x 40 mm x 350 mm BaF2:5%Y (mole fraction) crystals were grown by vertical Bridgman method. The doping content, scintillation properties, optical properties and irradiation damage of crystal samples were studied. The Y3+ doping concentration (mole fraction) is 5. 1% ± 0. 9% within the range from 0 to 300 mm from seed end. The average light output of crystal sample is 2 100 ph / MeV, and the optimal energy resolution at 662 keV is 10. 1%. After 60Co source was used to irradiate the sample with an accumulated dose of 1 Mrad, the transmittance of the sample at 220 nm wavelength decreases from 87. 3% before irradiation to 83. 5%, the transmittance at 300 nm wavelength decreases from 91. 8% to 89. 9%. The anti-irradiation performance of BaF2:Y crystal is worse than that of BaF2 crystal. After the accumulative dose irradiation, the absorption of BaF2:Y crystal to 300 nm light is significantly enhanced. [ABSTRACT FROM AUTHOR]