ВЗАЄМОДІЯ РОЗЧИНЕНОГО ВОДНЮ З ДИСЛОКАЦІЙНОЮ СТРУКТУРОЮ НИЗЬКОВУГЛЕЦЕВОГО НАПЛАВЛЕНОГО МЕТАЛУ.

The paper gives the results of studying [H]dif interaction in low-carbon metal, deposited by coated electrodes, with the dislocation structure of metal at plastic deformation during cooling in the range from 370 to 20 °С. [H]dif content was determined by thermodesorption analysis with chromatographic termination. [H]disl formation was found during deposited metal cooling at deformation temperature below 100 and up to 20 °С. Sample cooling method to determine [H]dif content corresponded to ІSO 3690 standard, and ensured [H]disl formation in the deposited metal. Metal alloying by nickel, chromium, and molybdenum leads to increase of [H]disl content. 21 Ref., 7 Tabl., 1 Fig. [ABSTRACT FROM AUTHOR]