The Effect of Physical Separation and Calcination on Enrichment and Recovery of Critical Elements from Coal Gangue.

Critical metallic elements in coal gangue have great utilization potential, especially due to the current shortage of these metals. This paper focused on examining the feasibility of physical separation (screening and float-sink tests) and calcination treatment for the enrichment of critical elements (Li, Ga, and rare earth elements plus yttrium (REY)) from coal gangue. The impacts of these enrichment methods on the acid leaching recovery of these elements were then studied. Screening tests indicated that Li and Ga were enriched in >0.125 mm size fraction and the content of REY was highest in <75 μm size fraction. Float-sink tests showed that high-density fractions were enriched in Li and Ga, and low-density fractions were enriched in REY. Physical separation cannot significantly improve the leaching rate of Li, Ga, and REY. Notably, Li, Ga, and REY were enriched significantly, and their acid leaching recoveries were increased by 54~68% after calcination under 400 °C. Sequential chemical extraction tests showed that the majority of insoluble Li, Ga, and REY was converted into soluble forms at the above temperature, which is attributed to the formation of amorphous metakaolinite and the decomposition of organic matter. Based on the results, a conceptually combined flowsheet was proposed for the extraction of Li and Ga from coal gangue. [ABSTRACT FROM AUTHOR]