Fabrication of sub-micrometer sized Er:CaF2 transparent ceramics for eye-safe lasers.
- Source :
-
Optical Materials . Nov2022, Vol. 133, pN.PAG-N.PAG. 1p. - Publication Year :
- 2022
-
Abstract
- The 1 at.% Er:CaF 2 transparent ceramics were prepared by the air pre-sintering and hot isostatic pressing (HIP) using nano-powders synthesized by the co-precipitation method. The influence of pre-sintering temperature and HIP post-treatment on the density, microstructures, optical and photoluminescence properties of Er:CaF 2 ceramics were investigated. After HIP post-treatment (650 °C × 2 h, 100 MPa Ar), the pores in the pre-sintering ceramics were gradually eliminated and high transparency was achieved. The maximum in-line transmittance of the HIPed 1 at.% Er:CaF 2 reaches 90.5% at 1600 nm (2.8 mm thickness) when the pre-sintered temperature is 625 °C.The absorption cross section was calculated. The strong absorption peak at 1530 nm reveals an unfavorable infrared emission. The main emission peak at 1530 nm, which is derived from the 4I 13/2 → 4I 15/2 transition of Er3+, can be observed under excitation of 980 nm. Owing to the long lifetime of 4I 13/2 (32.3 ms) and large emission cross section, the 1 at.% Er:CaF 2 transparent ceramics have great potential to achieve a good NIR laser performance in the 1.5 μm region. • Er:CaF 2 transparent ceramics were prepared by air pre-sintering and HIP post-treatment. • Fine-grain Er:CaF 2 transparent ceramics with uniform distribution were obtained. • Er:CaF 2 transparent ceramics showed high in-line transmittance of 90.5% at 1600 nm. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 09253467
- Volume :
- 133
- Database :
- Academic Search Index
- Journal :
- Optical Materials
- Publication Type :
- Academic Journal
- Accession number :
- 159755126
- Full Text :
- https://doi.org/10.1016/j.optmat.2022.113052